Candle sizes coming out of the mold: 3.5cm (diameter) x 0.9 cm (thickness) - Weight of the candle: 8 g (total) - Mold weight: 40 g - You can get 2 lotus flower-shaped candles in one casting.

They are high quality thick molds that can also be used in fragrance and soap making.

KOKULUTAŞ CONCRETE SOAP IS SUITABLE FOR CASTINGS.

OUR MOLDS ARE FLEXIBLE AND DURABLE.

(WHEN POURING SCENTED STONE, YOU SHOULD FIRST PUT THE WATER IN THE MIXING BOWL IN PROPORTION TO THE AMOUNT TO BE MADE.

THEN YOU SHOULD ADD THE POWDER PROPORTIONALLY ON THE WATER.

RATE (3/1 OR 4/1) IS THE GENERAL RATE OF 3 PARTS POWDER 1 PART WATER OR 4 PARTS POWDER 1 PART WATER.

THIS RATIO VARIES ACCORDING TO THE QUALITY OF TAŞTOZU.

CARE SHOULD BE TAKEN TO ENSURE THAT THE MIXING PROCESS IS FAST AND CAREFUL.

AFTER COMPLETING THE MIXTURE IN A WAY THAT THERE IS NO RESIDUE IN THE MIXTURE, YOU CAN GET A HEALTHY RESULT WITHIN 10-15 MINUTES BY ADDING HAMMADEY TO THE MOLD.

HOBBY PAINTS SHOULD NOT BE ADDED DIRECTLY TO THE OBJECTS YOU WANT TO OBTAIN COLORED IN THE MIXTURE.

OTHERWISE THE REACTION SLOWS DOWN AND THE PRODUCT FREEZES LATE.

AND 1 DROP OF ESSENCE WILL BE SUFFICIENT DURING THE ADDITION PHASE.

A LARGE AMOUNT OF THE ESSENCE AGAIN ACTS ON THE REACTION, SLOWING DOWN FREEZING.

(Raw material should be melted in belmari method for candle making.

The raw material should be allowed to cool down for a few minutes.

Then you can add pigment to the candles you want to color.

When using powder pigment, the raw material and the pigment should be mixed for 1- 2 minutes until the pigment is dispersed in the raw material.

Otherwise, roughness may occur on the object coming out of the mold.